8407 die steel is imported from the origin of Sweden, a chromium, molybdenum, vanadium hot work alloy die casting die steel, Sweden ASSAB 8407 die steel is divided into 8407 2M and 8407 SUPREME ESR two models, 8407 2M (i.e.: 8407) die steel using special steelmaking technology and strict quality control to get the purity and organization of the die steel material, than the general traditional Refining of H13 mold steel for the parameters of performance is better, the main features are: high and low temperatures have good wear resistance, excellent toughness and ductility, stable and excellent machinability and polished, excellent high-temperature strength and resistance to thermal fatigue, excellent hardenability and heat treatment deformation is very small.

At present 8407 is mainly used in: 1. Plastic molds (injection molds and compression mold transfer mold is recommended to use the hardness of 50-52HRC) 2. Extrusion molds (die kernel is recommended to use hardness of 45-50HRC; die bracket, die seat, bushings, slider, top rod is recommended to 40-48HRC) 3. Thick steel plate cold punching (scrap shear, hot shear recommended hardness 45-52HRC) 4. Mold rings (such as ceramic carbide mold recommended hardness 45-50HRC) 5. Wear-resistant parts (recommended hardness 50-52HRC) 6. Die-casting molds, forging molds, etc.
1. Khuôn nhựa (nên sử dụng độ cứng 50-52HRC cho khuôn ép phun và khuôn chuyển khuôn nén)
2. Khuôn ép đùn (lõi khuôn được khuyến nghị có độ cứng 45-50HRC; giá đỡ khuôn, đế khuôn, ống lót, thanh trượt và chốt đẩy được khuyến nghị có độ cứng 40-48HRC)
3. Đục nguội các tấm thép dày (độ cứng 45-52HRC được khuyến nghị để cắt thép phế liệu và cắt nóng)
4. Vòng đệm khuôn (chẳng hạn như khuôn cacbua gốm, nên sử dụng độ cứng 45-50HRC)
5. Các bộ phận chống mài mòn (khuyên dùng độ cứng 50-52HRC)
6. Khuôn đúc, khuôn rèn, v.v.